| Parker Compund: | FF200-75 |
| Temperature Range: | -15°C to 320°C (5°F to 608°F) |
| Test Samples: | 2-214 Size O-Rings |
| Specifications: | Gerneral Properties |
| Compound Description: | Black, Ultra High Temperature, 75 Shore A Parofluor Ultra™, Perfluorinated Elastomer |
| Property | Typical Results |
| Original Properties, ASTM D1414 Shore A Hardness Tensile Strength, MPa Elongation, % Modulus at 100% Elongation, MPa |
79 12.0 124 7.8 |
| Compression Set, 70 hours at 200°C, ASTM D395 Method B, 2-214 Size O-Rings % Permanent Set |
12 |
| Compression Set, 70 hours at 316°C, ASTM D395 Method B, 2-214 Size O-Rings % Permanent Set |
45 |
| Low Temperature Retraction, ASTM D1329 TR-10 in degress C |
-2 |
| Volume Change, 70 hours at room temperature, ASTM D471 Acetone, % Volume Change Methyl Ethyl Ketone, % Volume Change Methanol, % Volume Change Benzene, % Volume Change Toluene, % Volume Change Dichloromethane, %Volume Change Chloroform, % Volume Change Ethyl Acetate, % Volume Change MTBE, % Volume Change Glacial Acetic Acid, % Volume Change Conc. Phosphoric Acid, % Volume Change 50/50 by Volume, MEK/Methanol, %Volume Change Tetrahydrofuran (THF), % Volume Change Styrene Monomer, % Volume Change Methyl Methacrylate Monomer, % Volume Change |
0.4 0.2 0.2 0.3 0.3 0.6 0.6 0.4 0.2 0.4 0.0 0.7 0.4 0.0 0.5 |