| Parker Compound: | FF352-75 |
| Temperature Range: | -15°C to 316°C (5°F to 600°F) |
| Specifications: | General Properties |
| Compound Description: | White, Higb Temperature, 75 Shore A Parofluor ULTRA™, Perfluorinated Elastomer |
| Property | Typical Results |
| Original Properties, ASTM D1414 Shore A Hardness Tensile Strength, MPa Elongation, % Modulus at 100% Elongation, MPa |
76.0 16.9 142 9.2 |
| Compression Set, 70 hours at 200°C, ASTM D395 Method B, 2-214 Size O-Rings % Permanent Set |
16 |
| Compression Set, 70 hours at 260°C, ASTM D395 Method B, 2-214 Size O-Rings % Permanent Set |
28 |
| Low Temperature Retraction, ASTM D1329 TR-10 in degrees C |
-1 |
| Volume Change, 70 hours at room temperature, ASTM D471 Acetone, % Volume Change Methyl Ethyl Ketone, % Volume Change Methanol, % Volume Change Benzene, % Volume Change Toluene, % Volume Change Dichloromethane, % Volume Change Chloroform, % Volume Change Ethyl Acetate, % Volume Change MTBE, % Volume Change Glacial Acetic Acid, % Volume Change Conc. Phosphoric Acid, % Volume Change 50/50 by Volume, MEK/Methanol, % Volume Change tetrahydrofuran (THF), % Volume Change Styrene Monomer, % Volume Change Methyl Methacrylate Monomer, % Volume Change |
0.2 0.1 0.1 0.2 0.2 0.3 0.4 0.3 0.2 0.0 0.1 0.5 0.4 0.2 0.3 |